Charged Droplets Can Cause Surface Corrosion
Drops can become electrically charged as they slide across surfaces. If they then fall onto a coating-such as on a car-the coating can be corroded by the drop’s electrical discharge and permanently damaged.
© Katharina Maisenbacher / MPI for Polymer Research
To the point:
- Friction electricity: Water droplets that glide across plastic or leaf surfaces become electrically charged.
- Previously unknown corrosion: Charged droplets can damage coatings-such as paint-and the metals beneath them.
- The basis for corrosion protection: Understanding this form of corrosion could help in the development of coatings that protect against it.
Many people are familiar with this from everyday life: the paint on a garden fence needs to be repainted after a few years-“the weather has taken its toll.” But even larger structures, from the Eiffel Tower to the Golden Gate Bridge, must be time-consuming repainted to maintain them. Until now, two main causes were considered the driving forces behind such damage to coatings: first, mechanical stress-that is, a kind of friction between droplets and the surface that gradually wears down the coating or causes it to flake off; and second, chemical factors, particularly when droplets contain acids or salts.
Researchers led by Hans-Jürgen Butt, director at the Max Planck Institute for Polymer Research, have now identified another, previously unknown factor in collaboration with partners from the University of Bonn, South China University of Technology, MIT, and Johannes Gutenberg University Mainz: the electrical charge of droplets. “A few years ago, we investigated the physics behind how water droplets become charged as they slide across surfaces. This is a kind of ‘friction electricity’ in droplets and is physically much more complex than previously assumed,” says Rüdiger Berger, group leader in the “Physics at Interfaces” department. “When such charged droplets strike a coating, they discharge locally and can puncture the layer in specific spots like a small flash of lightning-with consequences for the coating’s durability.”
To demonstrate the damage caused by such electrical breakdowns, the researchers first dropped droplets specifically onto a surface uniformly coated with Teflon-a material commonly found on frying pans. With uncharged droplets, no changes to the coating were visible under the microscope even after 3,000 impacts. They then had the droplets roll across various everyday surfaces before impact-including a houseplant leaf, PVC, and polystyrene, such as that found in plastic windows. As they slid across these materials, the droplets became charged and subsequently fell onto the Teflon coating. After 3,000 droplets, distinct changes to the surface and the underlying metal were visible under the microscope.
The degree of charging is determined by the specific surface
“The charge a droplet acquires as it slides depends heavily on the specific surface-we measured differences of up to a factor of ten,” explains Zhongyuan Ni, researcher at the Max Planck Institute for Polymer Research. “Regardless of this, we were able to detect changes in the coating in all experiments.”
The researchers hope that their findings, published in the journal Nature, will pave the way for new, more efficient coatings that can protect cultural heritage, cars, or even the garden fence at home for longer and more effectively